木工应用牌号表
木工应用牌号表
| 牌号 | 粘结相 | 晶粒度 | 密度 | 硬度 | 抗折力 | USA Code | ISO Code |
|---|---|---|---|---|---|---|---|
| （%） | g/cm3 | HRA | N/mm2 | ||||
| UH5 | 3 | 亚细 | 15.15 | 94.3 | 2600 | C4 | K01 |
| UH12 | 12 | 亚细 | 14.15 | 92.2 | 4000 | C1 | K40 |
| MH3 | 3.3 | 亚细 | 15.1 | 94.6 | 2400 | C4 | K01 |
| MH3 | 3.3 | 亚细 | 15.1 | 94.6 | 2400 | C4 | K01 |
| MH4 | 3.3 | 超细 | 15.2 | 94.6 | 2400 | C4 | K05 |
| MH5 | 4.8 | 超细 | 14.95 | 94.1 | 2400 | C4 | K05 |
| MH6 | 5 | 超细 | 14.95 | 93.6 | 2800 | C3 | K10 |
| MH10F | 10 | 超细 | 14.45 | 91.8 | 3800 | C2 | K30 |
| EH6 | 5 | 超细 | 14.85 | 93.6 | 2400 | C3 | K10 |
| CF10 | 6 | 细 | 14.9 | 92 | 3000 | C3 | K10 |
| CF10A | 6 | 细 | 14.9 | 92.7 | 3000 | C3 | K10 |
| CF10R | 6.5 | 细 | 14.85 | 92 | 2200 | C3 | K10 |
| CF20 | 8 | 细 | 14.7 | 91 | 3000 | C3 | K10 |
| CF20A | 8 | 细 | 14.65 | 91.9 | 3200 | C3 | K10 |
| CF30 | 10 | 细 | 14.45 | 91.2 | 3300 | C1 | K30 |
| CK10 | 6 | 中细 | 14.9 | 91.3 | 2100 | C3 | K10 |
| CK101 | 5 | 中细 | 15 | 92.1 | 2000 | C3 | K10 |
| CK15 | 7 | 中细 | 14.8 | 91 | 2300 | C2 | K20 |
| CK20 | 8 | 中细 | 14.7 | 90.2 | 2500 | C2 | K20 |
| CK30 | 9 | 中细 | 14.6 | 89.8 | 2600 | C1 | K30 |
| CK40 | 12 | 中细 | 14.3 | 88.8 | 2800 | C1 | K40 |
| CK301 | 7.8 | 粗 | 14.8 | 89 | 2250 | C1 | K30 |
| CK401 | 11.5 | 粗 | 14.3 | 87.6 | 2700 | C1 | K40 |
| CK402 | 15 | 中 | 14 | 87.6 | 3000 | C1 | K40 |
| CK402CH | 15 | 中粗 | 14 | 86.5 | 2800 | C1 | K40 |
木工用金工应用牌号
| 牌号 | 粘结相 | 晶粒度 | 密度 | 硬度 | 抗折力 | USA Code | ISO Code |
|---|---|---|---|---|---|---|---|
| （%） | g/cm3 | HRA | N/mm2 | ||||
| CX30 | 12 | 中细 | 11.9 | 91.6 | 2500 | P30 | |
| CP30 | 12 | 中细 | 11.4 | 91.6 | 2200 | P30 |
木工用金属陶瓷牌号
| 牌号 | 粘结相 | 晶粒度 | 密度 | 硬度 | 抗折力 |
|---|---|---|---|---|---|
| （%） | g/cm3 | HRA | N/mm2 | ||
| CMT70 | 16 | 细 | 7.3 | 92 | 2100 |
| CMT80 | 18 | 细 | 7.25 | 91 | 2250 |